The Masters Theses collection contains digital copies of AUT University masters theses deposited with the Library since 2002 and made available open access. From 2007 onwards, all theses for masters degrees awarded are required to be deposited in Tuwhera Open Theses & Dissertations unless subject to an embargo.

For theses submitted prior to 2007, open access was not mandatory, so only those theses for which the author has given consent are available in Tuwhera Open Theses & Dissertations. Where consent for open access has not been provided, the thesis is usually recorded in the AUT Library catalogue where the full text, if available, may be accessed with an AUT password. Other people should request an Interlibrary Loan through their library.

Browse

Browsing Masters Theses by Author "Abraham, Francis"

Now showing 1 - 1 of 1
  • Thumbnail Image
    Item
    Tensile Properties and Fracture Behaviour of Multipass Friction Stir Processed Al-7Si-0.3Mg Cast Alloy
    (Auckland University of Technology, 2012) Abraham, Francis; Chen, Zhan; Pasang, Timotius
    Friction Stir Welding (FSW) is a solid state joining process using a rotating cylindrical shoulder and threaded pin which is plunged into the work piece to traverse along the join line. Friction Stir Processing (FSP) is a comparatively new process derived from FSW, which can be used to refine and modify as-cast microstructures for superior properties. In the last decade, several researchers have attempted to evaluate the microstructure and properties inside the stir zone. However, it is important to explain the features occurring outside the stir zone, in particular during multipass FSP (MP-FSP). The aim of this proposed research is to explain the MP-FSP process parameters and their relations to mechanical properties of the processed material, and hence to explain the fracture behaviour of the MP-FSPed material. Experimentally, cast plates of A356 (Al-7Si- 0.3Mg) alloy were made. Initial set of experiments with a high tool rotation speed (ω rpm) was conducted to produce maximum stir zone area. However, on finding that this parameter was not suitable (as will be explained), lower ω range FSP experiments were conducted. First, single pass FSP experiments were carried out to understand the flow, particularly outside the stir zone followed by MP-FSP under varying process parameters. Tensile testing was conducted and factors/FS parameters relating to fracture strain, and thus the quality of MP-FSP stir zone were studied and fracture features were examined. It was found that the use of high ω values resulted in the less deformed cast material wedging up into the stir zone of the previous pass. This wedging resulted in low tensile fracture strain. Explanation of Si particle alignment due to wedging and subsequently causing low fracture strain will be given. It will be shown that reducing ω reduces the degree of wedging, as the downward stir flow reduces. However, low ω values are shown to have a detrimental effect, incapable of completely disrupting / healing of tunnel wall oxide films, thus resulting in low fracture strain. It will be shown that with the current FS condition, ω=1000 rpm is the optimum value.
Theses are protected by the Copyright Act 1994 (New Zealand). The thesis may be consulted by you, provided you comply with the provisions of the Act and the following conditions of use:
  • Any use you make of these documents or images must be for research or private study purposes only, and you may not make them available to any other person.
  • Authors control the copyright of their thesis. You will recognise the author’s right to be identified as the author of the thesis, and due acknowledgement will be made to the author where appropriate.
  • You will obtain the author’s permission before publishing any material from the thesis.